Functional heat sealant Dynaleo™ PR/CT Series

Characteristics
- Excellent adhesion to various base materials (metals, polar base materials, etc.)
- Excellent heat and humidity resistance, weather resistance, and moldability
- Coloring and curing temperature can be changed according to your request.
Lineup
In addition to regular products, we also have a lineup adhesives that can be bonded at low temperatures.
- Highly durable and weather resistant Dynaleo™ PR series
- High heat resistance and high molding Dynaleo™ CT series
Product name | Heat seal temperature | Heat resistance | Weatherability | Moldability |
---|---|---|---|---|
Dynaleo™ PR series | 170℃ | ◎ | ◎ | × |
Dynaleo™ PR series (low temperature adhesive type) | 100℃~120℃ | |||
Dynaleo™ CT series | 190℃ | ◎ | × | ◎ |
Dynaleo™ CT series (low temperature adhesive type) | 100℃~120℃ | |||
Conventional heat seal | 120℃~160℃ | △ | × | × |
Product physical properties
Highly durable and weather resistant Dynaleo™ PR series
- Heat seal adhesives with excellent durability (humid heat resistance, weather resistance) that does not deteriorate even in harsh environments exposed to sunlight, wind and rain
- We also have a track record in solar cell backsheet.
Weather resistant coating agent Dynaleo™ PRC/DPT series
Humid heat resistance | Adhesive strength maintained after 1000 hours at 85℃ and 85%RH |
---|---|
Weatherability | After S-Xe 1000h ΔE<2 |
Adhesion performance * 1 | PET | NY | AL | PC |
---|---|---|---|---|
substrate adhesion * 2 Cross-cut test, number of squares remaining: 100 squares |
100 | 100 | 95 | 100 |
* 1: Use Dynaleo PRC-002 (general grade)
* 2: Apply 3g/m2 (dry) and dry at 100°C for 1 minute
High heat resistance and high moldability Dynaleo™ CT series
- Heat seal adhesives with excellent adhesion between film and metal
- Processing and molding possible after lamination
Humid heat resistance | 125℃/30min.No peeling or whitening |
---|---|
Appropriate for coating | Prevents wrinkles and unevenness even when coating at 150m/min. |
Adhesion performance * 1 | PET | NY | AL | PC |
---|---|---|---|---|
substrate adhesion * 2 Cross-cut test, number of squares remaining: 100 squares |
100 | 100 | 100 | 100 |
Peel strength * 3 90° peeling, N/10mm |
Base material rupture |
Base material rupture |
2.5 | 1.0 |
* 1: Use Dynaleo CT-001 (general grade)
* 2: Apply 3g/m2 (dry) and dry at 100°C for 1 minute
* 3: 3 g/m2 (dry) coating, drying at 100°C for 1 minute, thermal ramification (190°C, 1m/min., 0.5MPa, 150°C aging for 20 minutes)
No lifting of adhesive layer even when molded after heat curing

Immediately after Rami

Aperture height 6mm

Aperture height 14mm
Example of use
By applying heat and pressure to a film coated with a functional heat seal adhesives, it is possible to bond different types.
- heated roll press

- heat press molding
Application examples: Automotive interior parts, solar cell related parts, building materials processing, etc.